Abstract : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
Fibrin clot membranes prepared from advanced platelet-rich fibrin (A-PRF) or concentrated growth factors (CGF), despite their relatively rapid biodegradability, have been used as bioactive barrier membranes for alveolar bone tissue regeneration. As the membranes degrade, it is thought that the growth factors are gradually released. However, the mechanical and degradable properties of these membranes have not well been characterized. The purpose of this study was to mechanically and chemically characterize these membranes.
A-PRF and CGF clots were prepared from blood samples collected from non-smoking, healthy donors and were compressed to form 1-mm-thick membranes. Platelet-poor plasma-derived fibrin (PPTF) clots were prepared by adding bovine thrombin to platelet-poor plasma. A tensile test was performed at the speed of 1 mm/min. Morphology of the fibrin fibers was examined by SEM. A digestion test was performed in PBS containing trypsin and EDTA.
In the tensile test, statistical difference was not observed in Young’s modulus, strain at break, or maximum stress between A-PRF and CGF. In strain at break, PPTF was significantly weaker than CGF. Likewise, fibrin fiber thickness and crosslink density of PPTF were less than those of other membranes, and PPTF degraded faster than others.
Although the centrifugal conditions are different, A-PRF and CGF are prepared by essentially identical mechanisms. Therefore, it is conceivable that both membranes have similar mechanical and chemical properties. Only PPTF, which was prepared by a different mechanism, was characterized as mechanically weaker and enzymatically more degradable.
Serial posts:
- Abstract : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
- Background : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [1]
- Background : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [2]
- Methods : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [1]
- Methods : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [2]
- Methods : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [3]
- Results : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
- Discussion : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [1]
- Discussion : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [2]
- Conclusions : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
- Abbreviations : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
- References : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [1]
- References : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [2]
- Author information : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [1]
- Author information : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF) [2]
- Rights and permissions : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
- About this article : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
- Table 1 Similarity in size and stretching property of A-PRF and CGF membranes : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
- Table 2 Comparison of water content of A-PRF, CGF, and PPTF clots : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
- Table 3 Summaries of preparation procedures, relative mechanical, degradation, and related properties of A-PRF, CGF and PPTF : Mechanical and degradation properties of advanced platelet-rich fibrin (A-PRF), concentrated growth factors (CGF), and platelet-poor plasma-derived fibrin (PPTF)
- Fig. 1. Surface microstructures of A-PRF, CGF, and fibrin clots prepared by PPP + CaCl2 and PPTF (fibrin clots prepared by PPP and thrombin). Similar observations were obtained from other three independent blood samples. Scale bar = 10 μm. Note: the same magnification (×9000) was used in all the SEM images shown here : Mechanical and degradation properties of advanced
- Fig. 2. Representative stress-strain curves for A-PRF and CGF membranes and mechanical properties (Young’s modulus, strain at break, and maximum stress) of A-PRF, CGF, and PPTF membranes. N = 3–9 : Mechanical and degradation properties of advanced
- Fig. 3. Enzymatic degradability of A-PRF, CGF, and PPTF membranes. Each membrane disk (φ8 mm, 1 mm thick) was immersed in PBS containing trypsin and incubated in a CO2 incubator. N = 4. The asterisks represent significant differences (P < 0.05) compared with A-PRF at the same time points : Mechanical and degradation properties of advanced