Removal torque testing (RTQ) evaluation according to surface characteristic of implants
Table 2: Zirconia dental implants
author: Zeynep zkurt, DDS, PhD Ender Kazazolu, DDS, PhD | publisher: drg. Andreas Tjandra, Sp. Perio, FISID
Table 2
investigator | surface characteristics of implants | results of RTQ |
---|---|---|
Gahlert, 2007 | Machined zirkonia | 25.9 N/cm |
Gahlert, 2007 | Sandblasted zirconie | 40.5 N/cm |
Gahlert, 2007 | SLA titanium | 105.2 N/cm |
Sennerby, 2005 | Machined zirconia | Significantly lower RTQ values |
Sennerby, 2005 | Surface-coated zirconia | |
Sennerby, 2005 | Titanium | |
Ferguson, 2008 | SLA titanium | 1884 N/mm |
Ferguson, 2008 | SLA + CaP-coated titanium | 1683 N/mm |
Ferguson, 2008 | SLA + anosdic plasma-treated titanium | 919 N/mm |
Ferguson, 2008 | SLA + biphosphonate-coated titanium | 1835 N/mm |
Ferguson, 2008 | SLA + collagen-coated titanium | 1593 N/mm |
Ferguson, 2008 | SLA zirconia | 1005 N/mm |
-
Serial posts:
- Zirconia Dental Implants: A Literature Review
- Introduction : Zirconia Dental Implants
- Materials & methods : Zirconia Dental Implants
- Results: Zirconia dental implants
- Osseointegration, histologic analyses, and BIC : zirconia dental implant
- Surface analyses : zirconia dental implants
- RTQ (removal torque testing): zirconia dental implants
- Strength: Zirconia dental implants
- Conclusion: zirconia dental implants
- Simpulan: implant gigi zirkonia
- Table 1 : zirconia dental implants
- Tabel 1 : implant gigi zirkonia
- Table 2: Zirconia dental implants